Copper	63 - 68.5
Iron	0.07 max
Lead	0.1 max
Remainder Each	Zn

Principal Design Features		Brasses (Copper-Zinc Alloy), Yellow Brass, 65%. C27000 hot-forms more readily and is stronger than C26000.

Applications		Primarily used for hot or cold-formed products.

Machinability		The machinability rating of this alloy is 10. (Where Alloy 360 FC Brass is 100).

Welding		Soldering is rated as "excellent", brazing is rated as "excellent", oxyacetylene welding is rated as "good", gas shielded arc welding is rated as "fair", coated metal arc welding is "not recommended", spot welding is rated as "good", seam welding is "not recommended" and butt welding is rated as "good".

Forging		The hot forgeability rating of this alloy is not given. (Forging Brass=100). The recommended hot working temperature for this alloy is not given.

Hot Working		This alloy's capacity for being hot formed is rated as "poor".

Cold Working		The capacity for cold working this alloy is rated as "excellent".

Annealing		The annealing temperature for this alloy is between 800 and 1400 F.

Physical Data : [top]

Density (lb / cu. in.)	0.306
Electrical Resistivity (microhm-cm (at 68 Deg F))	38.4
Melting Point (Deg F)	1660
Modulus of Elasticity Tension	15000

There is no Mechnical data available for this grade.

[top]
Nickel - www.nidi.org

Copper - www.copper.org

Titanium - www.titanium.org

Steel Lynx - www.mlc.lib.mi.us/~stewarca/steelynx.html

Disclaimer
This information is provided "as is" and Metal Suppliers Online, Inc. makes no warranty of any kind with respect to the subject matter or accuracy of the information contained herein. Metal Suppliers Online, Inc. specifically disclaims all warranties, expressed, implied or otherwise, including without limitation, all warranties of merchantability and fitness for a particular purpose.

In no event shall Metal Suppliers Online, Inc. be liable for any special, incidental, indirect or consequential damages of any kind or any damages whatsoever resulting from loss of use, data, profits, whether or not advised of the possibility of damage, and on any theory of liability, arising out of or in connection with the use of the information contained herein.

This publication may include technical inaccuracies or typographical errors. Changes may be periodically made to the information herein.